Magnetic Penetrant Testing
Surface breaking or very near surface discontinuities in ferromagnetic materials give rise to leakage fields when high levels of magnetic flux are applied. These leakage fields attract magnetic particles (finely divided magnetite) to themselves leading to the formation of an indication.
The magnetic particles may be visibly or fluorescently pigmented to provide contrast with the substrate or conversely the substrate may be lightly coated with a white background lacquer to contrast with the particles.
Fluorescent magnetic particles normally provide the greatest sensitivity in a liquid suspension, usually applied by spraying. In certain cases dry particles may be applied by a gentle jet of air. The technique is applicable only to ferromagnetic materials at a temperature below the Curie point (about 650°C).
The leakage field will be greatest for linear discontinuities at right angles to the magnetic field so for a comprehensive test the magnetic field must normally be applied in two directions, mutually perpendicular. The test is economical to carry out in terms of equipment cost and rapidity of inspection and the level of operator training required is relatively low.
Source :
CSWIP 3.1 - Welding Inspector WIS5, TWI Ltd, 2017.
Surface breaking or very near surface discontinuities in ferromagnetic materials give rise to leakage fields when high levels of magnetic flux are applied. These leakage fields attract magnetic particles (finely divided magnetite) to themselves leading to the formation of an indication.
The magnetic particles may be visibly or fluorescently pigmented to provide contrast with the substrate or conversely the substrate may be lightly coated with a white background lacquer to contrast with the particles.
Fluorescent magnetic particles normally provide the greatest sensitivity in a liquid suspension, usually applied by spraying. In certain cases dry particles may be applied by a gentle jet of air. The technique is applicable only to ferromagnetic materials at a temperature below the Curie point (about 650°C).
The leakage field will be greatest for linear discontinuities at right angles to the magnetic field so for a comprehensive test the magnetic field must normally be applied in two directions, mutually perpendicular. The test is economical to carry out in terms of equipment cost and rapidity of inspection and the level of operator training required is relatively low.
Advantages
- Inexpensive equipment
- Direct location of defect
- Surface conditions not critical
- Can be applied without power
- Low skill level
- Sub-surface defects found 1-2mm
- Quick, instant results
- Hot testing (using dry powder)
- Can be used in the dark (UV light)
Limitations
- Only magnetic materials
- May need to demagnetise components
- Access may be a problem for the yoke
- Need power if using a yoke
- No permanent record
- Calibration of equipment
- Testing in two directions required
- Need good lighting - 500 lux minimum
Magnetic Penetrant testing
Magnetic Fluorescence Penetrant testing
CSWIP 3.1 - Welding Inspector WIS5, TWI Ltd, 2017.